| 性能（Property） | 种类Type | 检验标准 Testing in accordance with | ||||
| KC-W | KC-D | |||||
| 典型砌筑部位 Typical place of installation | ||||||
| 蓄热室墙 隔墙 | 炉顶 立柱 炉门 蓄热室底 | |||||
| Heating wall with elevated temperature of operation | Heating walls, Oven tops, Regenerator walls and frontage | |||||
| 化学成分 Chemical composition | SiO2 | % | X | 按双方协商 as per mutual agreement according to manufacturer's indications | DIN51070 Part2 and Part3 | |
| Al2O3 + TiO2 | % | X | ||||
| 颗粒度 Grain Size Spread | < 0.063 mm | % | 按双方协商 as per mutual agreement according to manufacturer's indications | Paragraph 3.4.1 | ||
| 0.063 to 0.125 mm | % | |||||
| 0.125 to 0.25 mm | % | |||||
| 0.25 to 0.5 mm | % | |||||
| 0.5 to 1 mm | % | |||||
| 1 to 2 mm | % | X | ≤2 | |||
| >2 mm | % | X | = 0 | |||
| 稠度 Consistency | 混合用水量 Required mixing water relative to dry substance | ml/100g | X | ≤40 | Paragraph 3.5 | |
| 浸泡深度 Dip depth | mm | X | 按双方协商 as per mutual agreement according to manufacturer's indications | |||
| 干燥变化量 Remaining Change in Length by Drying | TS | % | X | ≥-5 | ≥-6 | Paragraph 3.6.1 |
| 硬化性能（常温抗弯强度） Hardening characteristics (Cold flexural strength) | KFB after drying 干燥后 110℃ | N/mm2 | X | ≥0.1 | Paragraph 3.6.2 | |
| KFB after burning 烧后 1100℃ | N/mm2 | X | ≥0.7 | |||
| 压缩变形量 Compressive flow (DFI) | Δ D25 < 1,000℃ | % | X | ≥-0.1 | Paragraph 3.6.2 and DIN51053 Part2 | |
| Δ D25< 1,000℃ | % | X | ≥-0.3 | |||